HIGH TENSILE STRENGTH STEEL ELECTRODE
Brand	Size(mm)	Equivalent Specification	Welding Position	Type Of Current	Typical Chemical Composition Of Deposited Metal(wt%)										Typical Mechanical Properties Of Deposited Metal				Application
Brand	Size(mm)	Equivalent Specification	Welding Position	Type Of Current	C	Mn	Si	P	S	Cr	Ni	Mo	V	Others	屈服强度 Y.P.(MPa)	T.S.（MPa)	E.L.(%)	I.V.(J)	Application
WS.E9018M	2.5/3.2/4.0/5.0	GB/T E6218-N3M1 AWS E9018M	PA,PB,PC,PD,PE,PF	DC+/AC	0.058	1.02	0.37	0.024	0.011	0.13	1.66	0.33	0.01	-	690	595	26	-50℃/85	For welding 620MPa grade high strength steel,the coat is iron powder low hydrogen type.
WS.E11018M	2.5/3.2/4.0/5.0	GB/T E7618-N4M2 AWS E11018M	PA,PB,PC,PD,PE,PF	DC+/AC	0.065	1.28	0.42	0.019	0.008	0.26	2.19	0.43	0.01	-	760	830	20	-50℃/80	For welding 760MPa grade high strength steel,the coat is iron powder low hydrogen type.

HIGH TENSILE STRENGTH STEEL ELECTRODE
Brand	Size(mm)	Equivalent Specification	Welding Position	Type Of Current	Typical Chemical Composition Of Deposited Metal(wt%)										Typical Mechanical Properties Of Deposited Metal				Application
Brand	Size(mm)	Equivalent Specification	Welding Position	Type Of Current	C	Mn	Si	P	S	Cr	Ni	Mo	V	Others	屈服强度 Y.P.(MPa)	T.S.（MPa)	E.L.(%)	I.V.(J)	Application
WS.E9018M	2.5/3.2/4.0/5.0	GB/T E6218-N3M1 AWS E9018M	PA,PB,PC,PD,PE,PF	DC+/AC	0.058	1.02	0.37	0.024	0.011	0.13	1.66	0.33	0.01	-	690	595	26	-50℃/85	For welding 620MPa grade high strength steel,the coat is iron powder low hydrogen type.
WS.E11018M	2.5/3.2/4.0/5.0	GB/T E7618-N4M2 AWS E11018M	PA,PB,PC,PD,PE,PF	DC+/AC	0.065	1.28	0.42	0.019	0.008	0.26	2.19	0.43	0.01	-	760	830	20	-50℃/80	For welding 760MPa grade high strength steel,the coat is iron powder low hydrogen type.