PRODUCTS
Professional manufacturer of special welding consumablesSTAINLESS STEEL FLUX-CORED WIRE |
|||||||||||||||||||
Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current/Gas | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
C | Cr | Ni | Mo | Mn | Si | P | S | Cu | Others | Y.P.(Mpa) | T.S.(Mpa) | E.L.(%) | I.V.(J) | ||||||
WFS-308 | 1.2/1.6 | GB/T TS308-FC11 AWS E308T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.029 | 19.82 | 9.61 | 0.01 | 1.24 | 0.63 | 0.018 | 0.008 | 0.01 | - | - | 610 | 41 | - | Used for welding stainless steel structural parts of the same type (06Cr19Ni10). |
WFS-308L | 1.2/1.6 | GB/T TS308L-FC11 AWS E308LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.022 | 19.51 | 9.47 | 0.01 | 1.52 | 0.77 | 0.019 | 0.003 | 0.01 | - | - | 590 | 43 | - | For welding 022Cr19Ni10 stainless steel and for corrosion resistant 06Cr18Ni11Ti stainless steel structural parts whose working temperature is lower than 300℃. |
WFS-308H | 1.2/1.6 | GB/T TS308H-FC11 AWS E308HT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.049 | 19.50 | 9.69 | 0.02 | 1.40 | 0.71 | 0.026 | 0.003 | 0.02 | - | - | 605 | 41 | - | Widely used in petrochemical and chemical plants, especially in the manufacture of rotary separators, catalytic cracking unit for the production of catalyst recycling pipelines. |
WFS-309L | 1.2/1.6 | GB/T TS309L-FC11 AWS E309LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.036 | 24.31 | 12.10 | 0.02 | 1.48 | 0.73 | 0.023 | 0.002 | 0.06 | - | - | 590 | 40 | - | For welding the same type of stainless steel structure, composite steel and dissimilar steel components, which are manufactured by petrochemical equipment with working temperature below 400℃, can also be used for caldding of transition layer. |
WFS-309LD | 1.2/1.6 | GB/T TS309L-FC10 AWS E309LT0-1 |
PA,PB | DC+/CO2 | 0.026 | 24.20 | 12.77 | 0.02 | 1.25 | 0.61 | 0.025 | 0.003 | 0.06 | - | - | 580 | 39 | - | For cladding of inner wall of hydrogenation reactor or pressure vessel and transition layer of clad plate. |
WFS-309LMo | 1.2/1.6 | GB/T TS309LMo-FC11 AWS E309LMoT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.035 | 24.18 | 12.58 | 2.57 | 1.57 | 0.57 | 0.014 | 0.003 | 0.01 | - | - | 585 | 37 | - | For welding ultra-low carbon stainless steel structure (such as urea converter lining), composite steel and dissimilar steel components with working temperature below 300℃.It can also be used for transition layer caldding. |
WFS-316L | 1.2/1.6 | GB/T TS316L-FC11 AWS E316LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.034 | 19.15 | 12.27 | 2.64 | 1.64 | 0.60 | 0.017 | 0.005 | 0.03 | - | - | 580 | 38 | - | It can be used to weld the same type of ultra-low carbon stainless steel structure (such as urea synthesis tower lining), and also can be used to weld dissimilar steel. |
WFS-317L | 1.2/1.6 | GB/T TS317L-FC11 AWS E317LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.025 | 18.30 | 13.7 | 3.3 | 1.73 | 0.41 | 0.018 | 0.005 | 0.02 | - | - | 560 | 34 | - | On the basis of 316L, the pitting corrosion resistance is better by adding 1%Mo. |
WFS-310 | 1.2 | GB/T TS310-FC11 AWS E310T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.12 | 25.78 | 20.25 | 0.01 | 2.41 | 0.59 | 0.011 | 0.003 | 0.01 | - | - | 595 | 38 | - | For high temperature resistant products, such as high temperature furnace, coal coking equipment, can also be used for clad surfacing and dissimilar steel welding. |
WFS-310(Basic) | 1.2 | GB/T TS310-FC11 AWS E310T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.12 | 25.28 | 20.18 | 0.06 | 2.41 | 0.20 | 0.013 | 0.005 | 0.02 | - | - | 590 | 40 | - | On the basis of 310, the crack resistance was improved by alkaline formulation. |
WFS-347L | 1.2/1.6 | GB/T TS347-FC11 AWS E347T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.022 | 19.66 | 9.38 | 0.02 | 1.45 | 0.64 | 0.019 | 0.002 | 0.01 | Nb+Ta:0.38 | - | 590 | 39 | - | For welding 06Cr18Ni11 corrosion-resistant stainless steel with titanium or niobium stability. |
WFS-347LD | 1.2/1.6 | GB/T TS347-FC10 AWS E347T0-1 |
PA,PB | DC+/CO2 | 0.021 | 19.95 | 9.81 | 0.01 | 1.44 | 0.46 | 0.017 | 0.001 | 0.01 | Nb+Ta:0.34 | - | 580 | 40 | - | Cladding corrosion resistant layer on inner wall of hot-wall hydrogenation reactor. |
WFS-312 | 1.2 | GB/T TS312-FC11 AWS E312T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.050 | 28.5 | 8.5 | 0.01 | 1.2 | 0.6 | 0.016 | 0.002 | 0.01 | - | - | 740 | 24 | - | It can be used for welding high nickel alloy and other metals, because of its excellent crack resistance. It can also be used for welding high carbon steel, tool steel, dissimilar steel and surfacing of transition layer. |
WFS-2209 | 1.2 | GB/T TS2209-FC1 AWS E2209T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.024 | 23.11 | 9.20 | 3.18 | 1.25 | 0.65 | 0.015 | 0.003 | 0.02 | N:0.16 | - | 750 | 28 | - | Austenite-ferrite duplex stainless steel is suitable for welding of SUS S2205 S31803 in petrochemical industry. |
WFS-2594 | 1.2 | GB/T TS2594-FC10 AWS E2594T0-1 |
PA,PB | DC+/CO2 | 0.023 | 25.55 | 9.61 | 3.67 | 0.73 | 0.61 | 0.021 | 0.008 | 0.02 | N:0.26 | - | 830 | 23 | - | Austenite-ferrite super duplex stainless steel with excellent pitting corrosion resistance is suitable for welding of UNS S32750 and other steels. |
WFS-198 | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.041 | 19.86 | 9.22 | 0.02 | 1.19 | 0.54 | 0.020 | 0.004 | 0.02 | - | - | 590 | 32 | - | It has high ferrite content, excellent thermal resistance and intergranular corrosion resistance. It is suitable for 304 stainless steel working below 300℃. |
WFS-385 | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/80%Ar+20%CO2 | 0.026 | 20.38 | 24.51 | 4.22 | 1.60 | 0.45 | 0.016 | 0.002 | 1.45 | - | - | 595 | 40 | - | Super austenitic stainless steel with excellent corrosion resistance. |
WFS-410NiMo | 1.2/1.6 | GB/T TS410NiMo-FC11 AWS E410NiMoT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.044 | 11.85 | 4.43 | 0.56 | 0.48 | 0.52 | 0.019 | 0.005 | 0.01 | - | - | 842 | 19 | - | It is suitable for wear-resistant and corrosion-resistant occasions such as turbine rotor valves with stricter requirements. |
WFS-253MA | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.051 | 21.49 | 10.35 | 0.15 | 0.79 | 1.80 | 0.016 | 0.004 | - | N:0.13 Re:0.025 |
- | 665 | 46 | - | Ferro-based 22%Cr-10%Ni alloy with rare earth element content of C, Si, N and Ce controlled has excellent oxidation resistance. It is suitable for industrial furnaces and furnaces, high temperature flue, exhaust gas emission devices, etc. |
WCS-409Ti | 1.0/1.2 | GB/T TS409-MM131 AWS EC409 |
PA,PB,PC,PD,PE,PF | DC+/Ar | 0.047 | 11.04 | 0.01 | 0.01 | 0.54 | 0.36 | 0.011 | 0.008 | 0.01 | Ti:0.59 | - | 490 | 19 | - | Metal core flux cored wire is suitable for cold end welding of automobile exhaust system and muffler. |
STAINLESS STEEL FLUX-CORED WIRE |
|||||||||||||||||||
Brand | Size(mm) | Equivalent Specification | Welding Position | Type Of Current/Gas | Typical Chemical Composition Of Deposited Metal(wt%) | Typical Mechanical Properties Of Deposited Metal | Application | ||||||||||||
C | Cr | Ni | Mo | Mn | Si | P | S | Cu | Others | Y.P.(Mpa) | T.S.(Mpa) | E.L.(%) | I.V.(J) | ||||||
WFS-308 | 1.2/1.6 | GB/T TS308-FC11 AWS E308T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.029 | 19.82 | 9.61 | 0.01 | 1.24 | 0.63 | 0.018 | 0.008 | 0.01 | - | - | 610 | 41 | - | Used for welding stainless steel structural parts of the same type (06Cr19Ni10). |
WFS-308L | 1.2/1.6 | GB/T TS308L-FC11 AWS E308LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.022 | 19.51 | 9.47 | 0.01 | 1.52 | 0.77 | 0.019 | 0.003 | 0.01 | - | - | 590 | 43 | - | For welding 022Cr19Ni10 stainless steel and for corrosion resistant 06Cr18Ni11Ti stainless steel structural parts whose working temperature is lower than 300℃. |
WFS-308H | 1.2/1.6 | GB/T TS308H-FC11 AWS E308HT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.049 | 19.50 | 9.69 | 0.02 | 1.40 | 0.71 | 0.026 | 0.003 | 0.02 | - | - | 605 | 41 | - | Widely used in petrochemical and chemical plants, especially in the manufacture of rotary separators, catalytic cracking unit for the production of catalyst recycling pipelines. |
WFS-309L | 1.2/1.6 | GB/T TS309L-FC11 AWS E309LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.036 | 24.31 | 12.10 | 0.02 | 1.48 | 0.73 | 0.023 | 0.002 | 0.06 | - | - | 590 | 40 | - | For welding the same type of stainless steel structure, composite steel and dissimilar steel components, which are manufactured by petrochemical equipment with working temperature below 400℃, can also be used for caldding of transition layer. |
WFS-309LD | 1.2/1.6 | GB/T TS309L-FC10 AWS E309LT0-1 |
PA,PB | DC+/CO2 | 0.026 | 24.20 | 12.77 | 0.02 | 1.25 | 0.61 | 0.025 | 0.003 | 0.06 | - | - | 580 | 39 | - | For cladding of inner wall of hydrogenation reactor or pressure vessel and transition layer of clad plate. |
WFS-309LMo | 1.2/1.6 | GB/T TS309LMo-FC11 AWS E309LMoT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.035 | 24.18 | 12.58 | 2.57 | 1.57 | 0.57 | 0.014 | 0.003 | 0.01 | - | - | 585 | 37 | - | For welding ultra-low carbon stainless steel structure (such as urea converter lining), composite steel and dissimilar steel components with working temperature below 300℃.It can also be used for transition layer caldding. |
WFS-316L | 1.2/1.6 | GB/T TS316L-FC11 AWS E316LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.034 | 19.15 | 12.27 | 2.64 | 1.64 | 0.60 | 0.017 | 0.005 | 0.03 | - | - | 580 | 38 | - | It can be used to weld the same type of ultra-low carbon stainless steel structure (such as urea synthesis tower lining), and also can be used to weld dissimilar steel. |
WFS-317L | 1.2/1.6 | GB/T TS317L-FC11 AWS E317LT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.025 | 18.30 | 13.7 | 3.3 | 1.73 | 0.41 | 0.018 | 0.005 | 0.02 | - | - | 560 | 34 | - | On the basis of 316L, the pitting corrosion resistance is better by adding 1%Mo. |
WFS-310 | 1.2 | GB/T TS310-FC11 AWS E310T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.12 | 25.78 | 20.25 | 0.01 | 2.41 | 0.59 | 0.011 | 0.003 | 0.01 | - | - | 595 | 38 | - | For high temperature resistant products, such as high temperature furnace, coal coking equipment, can also be used for clad surfacing and dissimilar steel welding. |
WFS-310(Basic) | 1.2 | GB/T TS310-FC11 AWS E310T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.12 | 25.28 | 20.18 | 0.06 | 2.41 | 0.20 | 0.013 | 0.005 | 0.02 | - | - | 590 | 40 | - | On the basis of 310, the crack resistance was improved by alkaline formulation. |
WFS-347L | 1.2/1.6 | GB/T TS347-FC11 AWS E347T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.022 | 19.66 | 9.38 | 0.02 | 1.45 | 0.64 | 0.019 | 0.002 | 0.01 | Nb+Ta:0.38 | - | 590 | 39 | - | For welding 06Cr18Ni11 corrosion-resistant stainless steel with titanium or niobium stability. |
WFS-347LD | 1.2/1.6 | GB/T TS347-FC10 AWS E347T0-1 |
PA,PB | DC+/CO2 | 0.021 | 19.95 | 9.81 | 0.01 | 1.44 | 0.46 | 0.017 | 0.001 | 0.01 | Nb+Ta:0.34 | - | 580 | 40 | - | Cladding corrosion resistant layer on inner wall of hot-wall hydrogenation reactor. |
WFS-312 | 1.2 | GB/T TS312-FC11 AWS E312T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.050 | 28.5 | 8.5 | 0.01 | 1.2 | 0.6 | 0.016 | 0.002 | 0.01 | - | - | 740 | 24 | - | It can be used for welding high nickel alloy and other metals, because of its excellent crack resistance. It can also be used for welding high carbon steel, tool steel, dissimilar steel and surfacing of transition layer. |
WFS-2209 | 1.2 | GB/T TS2209-FC1 AWS E2209T1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.024 | 23.11 | 9.20 | 3.18 | 1.25 | 0.65 | 0.015 | 0.003 | 0.02 | N:0.16 | - | 750 | 28 | - | Austenite-ferrite duplex stainless steel is suitable for welding of SUS S2205 S31803 in petrochemical industry. |
WFS-2594 | 1.2 | GB/T TS2594-FC10 AWS E2594T0-1 |
PA,PB | DC+/CO2 | 0.023 | 25.55 | 9.61 | 3.67 | 0.73 | 0.61 | 0.021 | 0.008 | 0.02 | N:0.26 | - | 830 | 23 | - | Austenite-ferrite super duplex stainless steel with excellent pitting corrosion resistance is suitable for welding of UNS S32750 and other steels. |
WFS-198 | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.041 | 19.86 | 9.22 | 0.02 | 1.19 | 0.54 | 0.020 | 0.004 | 0.02 | - | - | 590 | 32 | - | It has high ferrite content, excellent thermal resistance and intergranular corrosion resistance. It is suitable for 304 stainless steel working below 300℃. |
WFS-385 | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/80%Ar+20%CO2 | 0.026 | 20.38 | 24.51 | 4.22 | 1.60 | 0.45 | 0.016 | 0.002 | 1.45 | - | - | 595 | 40 | - | Super austenitic stainless steel with excellent corrosion resistance. |
WFS-410NiMo | 1.2/1.6 | GB/T TS410NiMo-FC11 AWS E410NiMoT1-1 |
PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.044 | 11.85 | 4.43 | 0.56 | 0.48 | 0.52 | 0.019 | 0.005 | 0.01 | - | - | 842 | 19 | - | It is suitable for wear-resistant and corrosion-resistant occasions such as turbine rotor valves with stricter requirements. |
WFS-253MA | 1.2 | - | PA,PB,PC,PD,PE,PF | DC+/CO2 | 0.051 | 21.49 | 10.35 | 0.15 | 0.79 | 1.80 | 0.016 | 0.004 | - | N:0.13 Re:0.025 |
- | 665 | 46 | - | Ferro-based 22%Cr-10%Ni alloy with rare earth element content of C, Si, N and Ce controlled has excellent oxidation resistance. It is suitable for industrial furnaces and furnaces, high temperature flue, exhaust gas emission devices, etc. |
WCS-409Ti | 1.0/1.2 | GB/T TS409-MM131 AWS EC409 |
PA,PB,PC,PD,PE,PF | DC+/Ar | 0.047 | 11.04 | 0.01 | 0.01 | 0.54 | 0.36 | 0.011 | 0.008 | 0.01 | Ti:0.59 | - | 490 | 19 | - | Metal core flux cored wire is suitable for cold end welding of automobile exhaust system and muffler. |